电磁搅拌频率对 Cu-2Ag-0.04La 合金组织及性能的影响
(1.南昌航空大学航空制造工程学院，江西 南昌 330063;2.中国科学院金属研究所师昌绪先进材料创新中心, 辽宁 沈阳 110016;3.江西铜业技术研究院有限公司, 江西 南昌 330096;4.江西铜业股份有限公司, 江西 南昌 330096)
Effect of Electromagnetic Stirring Frequency on Microstructure and Properties of Cu-2Ag-0.04La Alloy
GUO Wei1,2, CHEN Yan3,4,5, HONG Zhi-yuan4, SONG Hong-wu2, WANG Ke-lu1, ZHANG Shi-hong2,5, QIU Qian1
(1.School of Aeronautical Manufacturing Engineering, Nanchang Aviation University, Nanchang 330063, Jiangxi, China;2.Shichangxu Advanced Materials Innovation Center, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China;3.Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, Liaoning, China;4.Jiangxi Copper Technology Research Institute Co., Ltd., Nanchang 330096, Jiangxi, China;5.Jiangxi Copper Company Limited,Nanchang 330096, Jiangxi, China)
摘要
图/表
参考文献
本刊相似文献
All Journals 相似文献
All Journals 引证文献
本文已被：浏览 1103次   下载 2156次
投稿时间：2021-10-08    
中文摘要: 采用真空连铸和电磁搅拌制备了直径 15 mm 的 Cu-2%Ag-0.04%La 合金棒坯，通过光学显微和力学拉伸试验研究了电磁搅拌频率对合金凝固组织、力学性能的影响。研究表明，随着搅拌频率的增加，枝晶尺寸逐渐增大。Cu-2%Ag-0.04%La 合金的硬度和抗拉强度随着搅拌频率的增加而降低，与频率为 10 Hz 的合金相比，抗拉强度降低 8.5 %，硬度降低 7.4 %。性能变化主要与横截面方向枝晶的数量和形貌有关。
中文关键词: Cu-Ag 合金  搅拌频率  稀土 La  微观组织  力学性能
Abstract:Cu-2%Ag-0.04%La alloy rod blank with a diameter of 15 mm was produced by vacuum continuous casting and electromagnetic stirring, the effect of electromagnetic stirring frequency and La addition on solidification microstructure, mechanical properties of alloys by optical microscopy and mechanical tensile test. Research shows that with the increase of stirring frequency, the dendrite size increases gradually. The hardness and tensile strength of the Cu-2%Ag-0.04%La alloy decrease with the increase of stirring frequency, Compared with the alloy with the frequency of 10 Hz, the tensile strength decreased by 8.5 %, and the hardness decreased by 7.4 %. It is mainly related to the number and morphology of dendrites in the cross section direction.
keywords: Cu-Ag alloy  mixing frequency  rare earth La  microstructure  mechanical property
文章编号：20220103     中图分类号：
基金项目:中国博士后科学基金资助项目（2019M662276）；中国科学院科技服务网络计划区域重点资助项目（KFJ-STS-QYZD-145）；江西省重大科技研发专项（20203ABC28W004）
引用文本： 郭伟,陈岩,洪志远,宋鸿武,王克鲁,张士宏,邱仟.电磁搅拌频率对 Cu-2Ag-0.04La 合金组织及性能的影响[J].铜业工程,2022,(1):10-13